Code
|
Related Standard
|
Chemical Composition
|
Impurity Amount
|
Melting Temperature
|
Major Characteristic
|
Typical Application
|
|
Ag %
|
Cu %
|
P %
|
Solidus℃
|
Liquidus℃
|
|
JAgP-1
|
CWA:BCu92PAg
|
0.9- 1.1
|
REM
|
6.8- 7.2
|
≤0.15
|
643
|
796
|
Lower solidus than Phos-copper brazing alloy. Improve wettability, strength and toughness.
|
Suitable for brazing copper and copper alloy parts.
|
|
JAgP-2
|
CWA:BCu91PAg
AWS:BCuP-6
|
1.8- 2.2
|
REM
|
6.8- 7.2
|
645
|
790
|
Good fluidity and brazing property, improve strength and good plasticity.
|
Suitable for brazing copper with copper alloy joints in freezer and air conditioner, suitable for brazing medium gap joints.
|
|
JAgP-5A
|
CWA:BCu88PAg
AWS:BCuP-7
|
4.6- 5.2
|
REM
|
6.8- 7.1
|
645
|
800
|
Improve strength, low phosphorus content result to liquidus with high temperature
|
Suitable for brazing copper and copper alloy parts, and brazing large gap joints.
|
|
JAgP-5A
|
CWA:BCu88PAg
AWS:BCuP-7
|
4.6- 5.2
|
REM
|
6.8- 7.1
|
645
|
765
|
Increase silver content can improve strength
|
Suitable for brazing shake copper with copper, copper with brass in air conditioner and freezer; brazing copper with copper alloy joints in electric motor and meter. With low phosphorus content suitable for brazing large gap joints; with high phosphorus content suitable for brazing small gap joints.
|
|
JAgP-15
|
CWA:BCu80PAg
|
14.5-15.5
|
REM
|
4.8- 5.3
|
645
|
800
|
Good fluidity.
|
Suitable for brazing copper and copper alloy joints with medium gap in air conditioner, freezer, compressor, electric motor etc.
|
|
JAgP-10
|
CWA:BCu84PAg
|
9.0- 11.0
|
REM
|
5.5- 6.5
|
645
|
790
|
Good fluidity and toughness.
|
Suitable for brazing copper with copper alloy in spectacle frame. Can be made into flat wire.
|
|
JAgP-5B
|
CWA:BCu89PAg
AWS:BCuP-3
|
4.8- 5.2
|
REM
|
5.8- 6.7
|
645
|
785
|
Increase silver content can improve strength
|
Suitable for brazing copper with copper alloy joints which cannot keep closely mate.
|